Excitation dependent multicolor emission and photoconductivity of Mn, Cu doped In2S3 monodisperse quantum dots.

Indium sulphide (In2S3) quantum dots (QDs) of average size 6 ± 2 nm and hexagonal nanoplatelets of average size 37 ± 4 nm have been synthesized from indium myristate and indium diethyl dithiocarbamate precursors respectively. The absorbance and emission band was tuned with variation of nanocrytal size from very small in the strong confinement regime to very large in the weak confinement regime. The blue emission and its shifting with size has been explained with the donor-acceptor recombination process. The 3d element doping (Mn(2+) and Cu(2+)) is found to be effective for formation of new emission bands at higher wavelengths. The characteristic peaks of Mn(2+) and Cu(2+) and the modification of In(3+) peaks in the x-ray photoelectric spectrum (XPS) confirm the incorporation of Mn(2+) and Cu(2+) into the In2S3 matrix. The simulation of the electron paramagnetic resonance signal indicates the coexistence of isotropic and axial symmetry for In and S vacancies. Moreover, the majority of Mn(2+) ions and sulphur vacancies (VS ) reside on the surface of nanocrystals. The quantum confinement effect leads to an enhancement of band gap up to 3.65 eV in QDs. The formation of Mn 3d levels between conduction band edge and shallow donor states is evidenced from a systematic variation of emission spectra with the excitation wavelength. In2S3 QDs have been established as efficient sensitizers to Mn and Cu emission centers. Fast and slow components of photoluminescence (PL) decay dynamics in Mn and Cu doped QDs are interpreted in terms of surface and bulk recombination processes. Fast and stable photodetctors with high photocurrent gain are fabricated with Mn and Cu doped QDs and are found to be faster than pure In2S3. The fastest response time in Cu doped QDs is an indication of the most suitable system for photodetector devices.

Carrier concentration dependent optical and electrical properties of Ga doped ZnO hexagonal nanocrystals.

Colloidal trivalent gallium (Ga) doped zinc oxide (ZnO) hexagonal nanocrystals have been prepared to introduce more carrier concentration into the wide band gap of ZnO. The dopant (Ga) modifies the morphology and size of ZnO nanocrystals. Low content of Ga enhances the optical band gap of ZnO due to excess carrier concentration in the conduction band of ZnO. The interaction among free carriers arising from higher concentration of Ga gives rise to narrowing of the band gap. Surface plasmon resonance absorption appears in the infrared region due to excessive carrier concentration. A broad emission band consists of blue, yellow and green colors associated with different native defects of ZnO. Intrinsic defects and extrinsic dopant Ga control the defect related emission spectrum in the visible region. Replacement of Zn by Ga induces a room temperature metallic state in a degenerate semiconductor. Cationic disorder leads to metal-semiconductor transition at low temperature strongly dependent on the concentration of Ga. Pure semiconducting behavior up to about 80 K is observed for the highest amount of Ga. Temperature dependent metal-semiconductor transition has been interpreted by localization of charge carriers due to disorder arising from random Ga substitution.

Interfacial magnetism and exchange coupling in BiFeO3-CuO nanocomposite.

Ferromagnetic BiFeO3 nanocrystals of average size 9 nm were used to form a composite with antiferromagnetic CuO nanosheets, with the composition (x)BiFeO3/(100-x)CuO, x = 0, 20, 40, 50, 60, 80 and 100. The dispersion of BiFeO3 nanocrystals into the CuO matrix was confirmed by x-ray diffraction and transmission electron microscopy. The ferromagnetic ordering as observed in pure BiFeO3 occurs mainly due to the reduction in the particle size as compared to the wavelength (62 nm) of the spiral modulated spin structure of the bulk BiFeO3. Surface spin disorder of BiFeO3 nanocrystals gives rise to an exponential behavior of magnetization with temperature. Strong magnetic exchange coupling between the BiFeO3 nanocrystal and the CuO matrix induces an interfacial superparamagnetic phase with a blocking temperature of about 80 K. Zero field and field cooled magnetizations are analyzed by a ferromagnetic core and disordered spin shell model. The temperature dependence of the calculated saturation magnetization exhibits three magnetic contributions in three temperature regimes. The BiFeO3/CuO nanocomposites reveal an exchange bias effect below 170 K. The maximum exchange bias field HEB is 1841 Oe for x = 50 at 5 K under field cooling of 50 kOe. The exchange bias coupling results in an increase of coercivity of 1934 Oe at 5 K. Blocked spins within an interfacial region give rise to a remarkable exchange bias effect in the nanocomposite due to strong magnetic exchange coupling between the BiFeO3 nanocrystals and the CuO nanosheets.